Key Features
Bambu Lab PA6-CF
The Bambu Lab PA6-CF filament is a high-performance material reinforced with carbon fiber, engineered for demanding applications requiring exceptional strength, heat resistance, and rigidity. This nylon-based filament is perfect for functional parts, automotive components, and other projects subjected to stress and high temperatures. PA6-CF is known for its low warping and dimensional stability, ensuring precise, durable prints. For optimal results, a hardened steel nozzle is recommended due to the abrasive nature of carbon fiber. Bambu Lab PA6-CF delivers industrial-grade quality, ideal for users seeking durability and functionality in their 3D printed parts.
Product Features
- Superior Strength and Stiffness
- Toughness & Vibration Resistance
- Exceptional Thermal Resistance
- Comes with High Temperature Reusable Spool
- Diameter: 1.75mm +/- 0.03mm
Cautions for Use
- 0.2 mm Nozzle Not Compatible
- Stainless Steel Nozzle Not Recommended
- Dry before Use for the Highest Print Quality
- AMS NOT Compatible
Superior Strength and Stiffness
As a new member of Bambu high performance filaments, PA6-CF keeps superior stiffness and strength properties in dry environments, it is perfect for printing load-bearing structural components.
| Normal PA-CF | PA6-CF | Improved % | |
| Strength (Bending Strength - XY, dry state) | 128 MPa | 151 MPa | 18% |
| Stiffness (Bending Modulus - XY, dry state) | 4420 MPa | 5460 MPa | 24% |
Impact & Vibration Resistance
Bambu PA6-CF offers excellent impact resistance, ensuring effective vibration resistance for your prints. It is commonly used to print models that need to withstand impact, collision, and vibration.
* The prints of PA6-CF will be tougher after putting in humid environment more than 1 day.
Exceptional Thermal Resistance
| Filament | PLA Basic | PETG Basic | ABS | ASA | PC | PA6-CF | PAHT-CF | PET-CF |
| Heat Deflection Temperature / (0.45 MPa) | 57 | 69 | 87 | 100 | 117 | 186 | 194 | 205 |
Printing Tips
Specifications
| Normal PA-CF | PA6-CF | Improved % | |
| Strength (Bending Strength - XY, dry state) | 128 MPa | 151 MPa | 18% |
| Stiffness (Bending Modulus - XY, dry state) | 4420 MPa | 5460 MPa | 24% |
Exceptional Thermal Resistance
| Filament | PLA Basic | PETG Basic | ABS | ASA | PC | PA6-CF | PAHT-CF | PET-CF |
| Heat Deflection Temperature / (0.45 MPa) | 57 | 69 | 87 | 100 | 117 | 186 | 194 | 205 |
Parameters Comparison
Learn more different filaments comparison on Bambu Filament Guide >>
| Normal PA6-CF | PA6-CF | PAHT-CF | |
| Composition | Nylon 6, carbon fiber | Nylon 6, carbon fiber | PA12 and other long-chain PA, carbon fiber |
| AMS Compatibility | NO | NO | YES |
| Dry Out Before Use | Required | Required | Required |
| Printing Speed | < 100 mm/s | < 100 mm/s | < 100 mm/s |
| Printer Type | Enclosure | Enclosure | Enclosure |
| Toughness (Impact Strength - XY, dry state) | 35.7 kJ/m | 40.3 kJ/m | 57.5 kJ/m |
| Toughness (Impact Strength - XY, wet state) | 65.4 kJ/m | 57.2 kJ/m | 62.3 kJ/m |
| Strength (Bending Strength - XY, dry state) | 141 MPa | 151 MPa | 125 MPa |
| Strength (Bending Strength - XY, wet state) | 67 MPa | 95 MPa | 115 MPa |
| Layer Strength (Bending Strength - Z, dry state) | 72 MPa | 80 MPa | 61 MPa |
| Layer Strength (Bending Strength - Z, wet state) | 31 MPa | 45 MPa | 49 MPa |
| Stiffness (Bending Modulus - XY, dry state) | 4870 MPa | 5460 MPa | 4230 MPa |
| Stiffness (Bending Modulus - XY, wet state) | 1890 MPa | 3560 MPa | 3640 MPa |
| Layer Adhesion (Impact Strength - Z, dry state) | 11.6 kJ/m | 15.5 kJ/m | 13.3 kJ/m |
| Heat Resistant HDT, 0.45 MPa | 177 | 186 | 194 |
| Saturated Water Absorption Rate / % (25 5% RH) | 3.80 | 2.35 | 0.88 |
| Recommended Printing Settings | |
| Drying Settings before Printing | 80 , 8 - 12 h |
| Printing and Keeping Container's Humidity | < 20% RH (Sealed, with Desiccant) |
| Nozzle Temperature | 260 - 290 |
| Bed Temperature (with Glue) | 80 - 100 |
| Printing Speed | < 100 mm/s |
| Physical Properties | |
| Density | 1.09 g/cm |
| Vicat Softening Temperature | 212 |
| Heat Deflection Temperature | 186 |
| Melting Temperature | 223 |
| Melt Index | 6.8 0.6 g/10 min |
| Mechanical Properties | |
| Tensile Strength | 102 7 MPa |
| Breaking Elongation Rate | 5.8 1.6 % |
| Bending Modulus | 5460 280 MPa |
| Bending Strength | 151 8 MPa |
| Impact Strength | 40.3 2.5 kJ/m |
Black - Bambu Lab PA6-CF Filament - 1.75mm