Liqcreate Rigid Pro is a rigid black photopolymer resin and can be processed on most open DLP, MSLA and laser based 3D-printers operating at a wavelength of 385-405nm. 3D-printed parts from this material exhibit high strength and rigidity. Liqcreate Rigid Pro only requires UV post-curing with heat to reach its optimal strength. This material has excellent features like: high stiffness, durability, high strength and good temperature resistance which makes it ideal for molding, and industrial applications like pulleys, automotive connectors, covers, brackets, housings and demanding engineering parts.
Scroll down to: Technical specifications | Printer compatibility |Â Use cases |Â Processing instructions
 |
 |
 |
|
High Strength |
Good temperature resistance |
Good chemical resistance |
Excellent thermal performance
Liqcreate Rigid Pro has a good heat deflection temperature (HDT) while maintining high strength. HDT values are depending on curing. A thermal post-cure is optional and will boost performance.
For extra details, download the technical data sheet or user guide.
| EAN | N/A |
| SKU | N/A |
| Tensile strength (UV curing 30 minutes at 60°C) | 52 – 70 MPa |
| Tensile strength (UV curing 120 minutes at 60°C) | 60 – 84 MPa |
| Tensile modulus (UV curing 30 minutes at 60°C) | 2.6 – 2.8 GPa |
| Tensile modulus (UV curing 120 minutes at 60°C) | 3.0 – 3.2 GPA |
| Elongation at break (UV curing 30 minutes at 60°C) | 4 – 8% |
| Elongation at break (UV curing 120 minutes at 60°C) | 3 – 6% |
| Flexural strength (UV curing 30 minutes at 60°C) | 100 – 110 MPa |
| Flexural strength (UV curing 120 minutes at 60°C) | 110 – 130 MPa |
| Flexural modulus (UV curing 30 minutes at 60°C) | 2.8 – 3.0 GPa |
| Flexural modulus (UV curing 120 minutes at 60°C) | 3.0 – 3.2 GPa |
| IZOD Impact (notched) D256A (UV curing 30 minutes at 60°C) | 21 J/m |
| IZOD Impact (notched) D256A (UV curing 120 minutes at 60°C) | 18 J/m |
| IZOD Impact (notched) ISO 180 (UV curing 30 minutes at 60°C) | 2.5 kJ/m2 |
| IZOD Impact (notched) ISO 180 (UV curing 120 minutes at 60°C) | 2.3 kJ/m2 |
| Water sorption (UV curing 30 minutes at 60°C) | 0.46% |
| Water sorption (UV curing 120 minutes at 60°C) | 0.40% |
| Shore D Hardness (UV curing 30 minutes at 60°C) | 87 |
| Shore D Hardness (UV curing 120 minutes at 60°C) | 90 |
| HDT-B 0.45 MPa (UV curing 30 minutes at 60°C) | 77°C / 171°F |
| HDT-B 0.45 MPa (UV curing 120 minutes at 60°C) | 91°C / 196°F |
| HDT-A 1.8 MPa (UV curing 30 minutes at 60°C) | 65°C / 133°F |
| HDT-A 1.8 MPa (UV curing 120 minutes at 60°C) | 75°C / 167°F |
| Appearance | Opaque black liquid |
| Viscosity | 290 mPa.s at 25°C |
| Density | 1.12 g/cm3 |
| Ec (405nm) | 8.76 mJ/cm2 |
| Dp (405nm) | 0.23 mm |
| Ec (385nm) | 3.43 mJ/cm2 |
| Dp (385nm) | 0.09 mm |
| Weight | N/A |
| Printer compatibility | SLA, DLP, LCD |
Liqcreate Rigid Pro - 1kg
All orders are shipped from and processed in Canada. Duties, taxes, tariffs, and credit card foreign transaction fees may apply.