Key Features
LOCTITE® 3D IND406™ is a high strength, high elongation engineering plastic with good impact and high temperature resistance.
Stiffness, toughness and thermal durability make this material ideal for a wide variety of tools in the production floor and for final parts production in automotive interior and manufacturing. The product is ideal for fixtures, interior and machinery parts.
LOCTITE® 3D IND406™ can be printed in various DLP printers and parts can be machined, patted of polished for final finish.
Specifications
Properties
| Mechanical Properties | Measure | Method | Green | Post Processed |
| Youngs Modulus | MPa | ASTM D638 | 360 50 [1] | 1610 40 [16] |
| Tensile Stress at Break | MPa | ASTM D638 | 17 3 [1] | 55 1 [16] |
| Elongation at Break | % | ASTM D638 | 40 6 [1] | 25 4 [2] |
| Flexural Modulus | MPa | ASTM D790 | 391 28 [21] | 1880 25 [21] |
| Flexural Stress at Break | MPa | ASTM D790 | - | - |
| Flexural Strain at Break | % | ASTM D790 | >5 [21] | >5[21] |
| IZOD Impact (Notched) | J/m | ASTM D256 | 75 4 [3] | 35 8 [4] |
| Shore Hardness | D | ASTM D2240 | 57 1 [6] | 79 1 [7] |
Other Properties
| HDT at 0.455 MPa | ASTM D648 | - | 107 1 [5,17] | |
| HDT at 1.82 MPa | ASTM D256 | - | 81 2 [5,17] | |
| Water Absorption (24 h) | % | ASTM D570 | - | 1.4 [8] |
| Water Absorption (72 h) | % | ASTM D570 | - | 2.6 [9] |
| Solid Density | g/cm | ASTM D792 | - | 1.19 [18] |
| Thermal Conductivity | mW/m*K | ASTM D5930 | - | 206 3 [14] |
| Heat Capacity | J/(g*K) | ASTM D5930 | - | 1.46 0.04 [14] |
| Horizontal Flame Spread Speed (1.4 mm thickness) | mm/min | DIN 75200 | - | 28 (Pass) [15] |
Biocompatibility
| Cytotoxicity | ISO10993-5 | Comply [19] | ||
| Irritation | ISO10993-23* | Comply [20] |