LOCTITE® 3D PRO476™ is a high strength plastic with good impact resistance, moderate heat resistance and excellent surface finish. This material is ideal for a variety of performance prototype and tooling applications and can be machined, tapped or polished for final finish.
LOCTITE® 3D PRO476™ is formulated to print optimally on LCD printers on a wavelength of 405nm.
Properties
| Mechanical Properties | Measure | Method | Green | Post Processed |
| Young’s Modulus | MPa | ASTM D638 | 360 ± 50 [1] | 1610 ± 40 [16] |
| Tensile Stress at Break | MPa | ASTM D638 | 17 ± 3 [1] | 55 ± 1 [16] |
| Elongation at Break | % | ASTM D638 | 40 ± 6 [1] | 25 ± 4 [2] |
| Flexural Modulus | MPa | ASTM D790 | 391 ± 28 [21] | 1880 ± 25 [21] |
| Flexural Stress at Break | MPa | ASTM D790 | - | - |
| Flexural Strain at Break | % | ASTM D790 | >5 [21] | >5[21] |
| IZOD Impact (Notched) | J/m | ASTM D256 | 75 ± 4 [3] | 35 ± 8 [4] |
| Shore Hardness | D | ASTM D2240 | 57 ± 1 [6] | 79 ± 1 [7] |
Other Properties
| HDT at 0.455 MPa | ℃ | ASTM D648 | - | 107 ± 1 [5,17] |
| HDT at 1.82 MPa | ℃ | ASTM D256 | - | 81 ± 2 [5,17] |
| Water Absorption (24 h) | % | ASTM D570 | - | 1.4 [8] |
| Water Absorption (72 h) | % | ASTM D570 | - | 2.6 [9] |
| Solid Density | g/cm³ | ASTM D792 | - | 1.19 [18] |
| Thermal Conductivity | mW/m*K | ASTM D5930 | - | 206 ± 3 [14] |
| Heat Capacity | J/(g*K) | ASTM D5930 | - | 1.46 ± 0.04 [14] |
| Horizontal Flame Spread Speed (1.4 mm thickness) | mm/min | DIN 75200 | - | 28 (Pass) [15] |