LOCTITE® 3D IND147™ is a high temperature resistant resin with HDT of 230°C and good dimensional stability for low loads processes in molding applications.
LOCTITE® 3D IND147™ shows good surface finish and sufficient toughness to withstand mechanical stresses from molding processes. It's unique properties make it ideal for applications such as polyurethane and silicone molding.
Benefits and Uses:
• High HDT >230°C
• Tough with good dimensional stability
• Good Surface Finish
• Ideal for tooling at high temperature, low pressure
• High temperature parts prototyping
• Customized molds
Properties
| Mechanical Properties | Measure | Method | Green | Post Processed |
| Young’s Modulus | MPa | ASTM D638 | 1150 ± 160 [2] | 3190 ± 80 [1] |
| Tensile Stress at Break | MPa | ASTM D638 | 31 ± 2 [2] | 67 ± 16 [1] |
| Elongation at Break | % | ASTM D638 | 6 ± 2 [2] | 2.4 ± 0.7 [1] |
| Poisson’s Ratio | - | ASTM D638 | - | 0.30 ± 0.03 [16] |
| Flexural Modulus | MPa |
ASTM D790 |
1170 ± 100 [1] | 3690 ± 60 [12] |
| Flexural Stress at Break | MPa | ASTM D790 | - | 120 ± 4 [12] |
| Flexural Strain at Break | % | ASTM D790 | >5 [11] | 3.5 ± 0.2 [12] |
| IZOD Impact (Notched) | J/m |
ASTM D256 |
- | 14.6 ± 0.1 [7] |
| Shore Hardness | D | ASTM D2240 | - | 94 [8] |
Other Properties
| HDT at 0.455 MPa | ℃ | ASTM D648 | - | 235 - 291 [15/13] |
| HDT at 1.82 MPa | ℃ |
ASTM D648 |
- | 136 - 163 [14] |
| Water Absorption (24hr) | % | ASTM D570 | - | 0.24 [9] |
| Water Absorption (72hr) | % | ASTM D570 | - | 0.39 [9] |
| Water Absorption (168hr) | % | ASTM D570 | - | 0.78 [9] |
| Solid Density | g/cm³ | ASTM D792 | 1.25 [10] | 1.26 [10] |
| Thermal Conductivity | W/(m*K) | ASTM D5930 | - | 0.20 [5] |
| Heat Capacity | J/(g*K) | ASTM D5930 | - | 1.3 [5] |
| CTE (-40℃ to 40℃) | μm/(m*K) | ASTM E831 | - | 114 [6] |